INFLUENCE OF POLYMERIC FOAM COMPOSITE "PENOCOM" ON FIRE RESISTANCE OF WOOD FRAME SEPARATING CONSTRUCTIONS
https://doi.org/10.18322/PVB.2016.25.01.28-37
Abstract
Sing a small-scale fire tests three separating construction assemblies modeling fragments of walls and partitions in timber buildings of light frame type have been studied. As a thermal insulation layer have used a commercial polymer foam composite "Penocom" with different density between 43.7-140 kg/m3. It was established that the actual limit of fire resistance of separating constructions for the integrity and insulating capacity (EI) was 95-110.3 min. It was found that there is a tendency: increasing the fire resistance of four-layers structures corresponds decreasing the density foam composites "Penocom" from 83 to 43.7 kg/m3. The average values of the heat flow in the small-scale fire oven at the standard mode of fire at different periods of fire actions have been measured as well. These values correspond the relationship found at standard large-scale apparatus. Thermal conductivity of polymer foam composite was calculated.
About the Authors
F. A. Shutov
D. Mendeleev University of Chemical Technology of Russia
Russian Federation
Russian Federation
E. Yu. Kruglov
State Fire Academy of Emercom of Russia
Russian Federation
Russian Federation
R. M. Aseeva
State Fire Academy of Emercom of Russia
Russian Federation
Russian Federation
B. B. Serkov
State Fire Academy of Emercom of Russia
Russian Federation
Russian Federation
A. B. Sivenkov
State Fire Academy of Emercom of Russia
Russian Federation
Russian Federation
References
1. Buchanan A., Ostman В., Frangi A. Fire resistance of timber structures: a report for the National Institute of Standards and Technology. URL: www.nist.gov/el/fire_research/upload/NIST-Timber-Report-v4-Copy.pdf (дата обращения: 20.10.2015).
2. Barber D., Gerard R. High-rise timber buildings // Fire Protection Engineering, July 2014. URL: http://www.sfpe.org/?page=2014_Q3_1 (дата обращения: 20.10.2015).
3. of the best wooden skyscrapers. URL: https://www.worldbuild365.com/news/detail/sawxeob2a/ building-architecture/10-of-the-best-wooden-skyscrapers (дата обращения: 20.10.2015).
4. Казейкин В. С, Баронин С. А., Черных А. Г., Андросов А. Н. Проблемные аспекты развития малоэтажного жилищного строительства в России. - М. : ИНФРА М, 2011. - 278 с.
5. Асеева Р. М., Серков Б. Б., Сивенков А. Б. Горение древесины и ее пожароопасные свойства. - М. : Академия ГПС МЧС России, 2010. - 262 с.
6. BS EN 1995-1-2:2004: Eurocode 5: Design of timber structure. Part 1-2: General - Structural fire design. - Belgium, Brussels: CEN, 2004.
7. Fire safety in timber buildins. Technical guideline for Europe / SP Report 2010:19. URL: http://euro-codes.jrc.ec.europa.eu/doc/Fire_Timber_Ch_5-7.pdf (дата обращения: 10.10.2015).
8. White R. H. Analytical methods for determining fire resistance of timber members // SFPE Handbook of Fire Protection Engineering. - New York : Springer, 2016. - P. 1979-2011. DOI: 10.1007/978-1-4939-2565-0_55.
9. White R. H. Fire resistance of wood with members with directly applied protection // Proceedings of 11th International Conference and Exhibition "Fire and Materials 2009". - UK, London : Interscience Communications, 2009. - 971 p. URL: http://naldc.nal.usda.gov/download/44930/PDF (дата обращения: 10.10.2015).
10. Покровская Е. Н., Портнов Ф. А., Кобелев А. А., Корольченко Д. А. Дымообразующая способность и токсичность продуктов сгорания древесных материалов при поверхностном модифицировании элементоорганическими соединениями // Пожаровзрывобезопасность. - 2013. - Т. 22, № 10.- С. 40-45.
11. Лукьянов А. М., Корольченко Д. А., Агапов А. Г. О пожароопасности древесины при возведении мостов // Мир транспорта. - 2012. - Т. 10, № 4 (42). - С. 158-162.
12. Сайт Hot Well. SIP-технологии. URL: www.hotwell.ru (дата обращения: 10.10.2015).
13. Fire resistance of timber frame wall construction // PU EUROPE excellence in insulation. - February 2013. - Factsheet no. 20. URL: http://ecotermix.ru/wp-content/uploads/2013/12/Test-PU-Europe.pdf (дата обращения: 10.10.2015).
14. Just A., Schmid J., König J. Gypsum plasterboards used as fire protection - analysis of a database / SP Report 2010:29. - Stockholm, 2010.
15. Sultan M. A. Factors affecting fire resistance performance of lightweight frame floor assemblies // Proceedings of 8th International Fire Science and Engineering Conference. Interflam'99. - Scotland, Edinburg, 1999. - P. 897-910.
16. Шутов Ф. А. Огнестойкие материалы для снижения пожарной опасности малоэтажных объектов из древесины // Технологии техносферной безопасности: интернет-журнал. - 2014. -№ 3 (55). URL: http://agps-2006.narod.ru/ttb/2014-3/22-03-14.ttb.pdf (дата обращения: 15.10.2015).
17. Шутов Ф. А., Ярборо Д. Теплоизоляционные и экологические характеристики огнестойкого полимерного пенокомпозита PENOCOM®// Технологии техносферной безопасности : интернет-журнал. - 2014. - № 4 (56). URL: http://agps-2006.narod.ru/ttb/2014-4/37-04-14.ttb.pdf (дата обращения: 15.10.2015).
18. Круглов Е. Ю., Шутов Ф. А., Асеева P. M., Серков Б. Б., Сивенков А. Б. Огнестойкость ограждающих легких деревянных каркасных конструкций с теплоизоляцией из пенокомпозита "Penocom" // Пожары и чрезвычайные ситуации: предотвращение, ликвидация. -2015. -№ 3. -С. 63-70.
19. СП 64.13330.2011. Деревянные конструкции (актуализированная ред. СНиП II-25-80). - Введ. 20.05.2011.-М. :ОАО"ЦПП", 2011.
20. Babrauskas K.Wood char depth: interpretation in fire investigations // Proceedings of International Symposium on Fire Investigation. United Kingdom, Moreton-in-Marsh: Fire Science and Technology Inc., 2004.- 12 p.
Review
For citations:
Shutov F.A., Kruglov E.Yu., Aseeva R.M., Serkov B.B., Sivenkov A.B. INFLUENCE OF POLYMERIC FOAM COMPOSITE "PENOCOM" ON FIRE RESISTANCE OF WOOD FRAME SEPARATING CONSTRUCTIONS. Pozharovzryvobezopasnost/Fire and Explosion Safety. 2016;25(1):28-37. (In Russ.) https://doi.org/10.18322/PVB.2016.25.01.28-37
Views:
552
Email this article 