INFLUENCE OF SURFACE LAYER STRUCTURE FORMED DURING THERMAL DEGRADATION OF WOOD ON SMOKE GENERATION PROPERTY
Abstract
Wood-hazard material that generate a lot of smoke in case of fire. In combination with toxic gases of thermal degradation it may result in destructive consequences include deaths. Some fire retardants are capable to change thermal degradation process of wood reducing the number of smoke. In that paper influence of phosphorus-containing compounds on smoke generation have been considered. In paper there are used some of the physico-chemical methods (porous structure methods BET/BJH, IR-spectroscopy, elemental analysis) and standard method for determination of smoke generation properties of building materials. In the result the most effective compound and offered the mechanism of effective smoke suppression in the presence of diethylphosphate are selected. Wood with diethylphosphite in case of fire has the minimal smoke generation. This effect can be explain by analysis of porous structure of surface layer after thermal degradation. Results of elemental analysis and IR-spectroscopy indicate high content of elemental phosphorus in the surface layer.
Keywords
древесина,
фосфорсодержащие соединения,
эфиры фосфористой кислоты,
поверхностная модификация,
дымообразующая способность,
пористая структура поверхностного слоя,
wood,
timber,
phosphorus-containing compounds,
esters of phosphorous acid,
surface modification,
smoke generation property,
porous structure,
thermal degradation
About the Authors
E. N. Pokrovskaya
Moscow State University of Civil Engineering
Russian Federation
Russian Federation
F. A. Portnov
Moscow State University of Civil Engineering
Russian Federation
Russian Federation
A. A. Kobelev
State Fire Service Academy of Emercom of Russia
Russian Federation
Russian Federation
T. G. Beltsova
Moscow State University of Civil Engineering
Russian Federation
Russian Federation
References
1. Ушков В. А., Невзоров Д. И., Копытин А. В., Лалаян В. М. Воспламеняемость и дымообразующая способность полимерных материалов, содержащих производные ферроцена // Пожаровзрыво-безопасность. - 2014. - Т. 23, №№ 7. - С. 27-35.
2. Щеглов П. П., Иванников В. Л. Пожароопасность полимерных материалов. - М. : Стройиздат, 1992.- 110 с.
3. Butcher E. G., Parnell A. C. Smoke control in fire safety design. - London : E. & F. N. Spon, 1979. - 178 p.
4. Асеева P. М., Серков Б. Б., Сивенков А. Б. Горение древесины и ее пожароопасные свойства: монография. - М. : Академия ГПС МЧС России, 2010. - 262 с.
5. Асеева P. М., Заиков Г. Е. Горение полимерных материалов. - М. : Наука, 1981. - 280 с.
6. Пожары и пожарная безопасность в 2011 году. Статистика пожаров и их последствий : статистический сборник. - М. : ВНИИПО МЧС России, 2012. - 137 с.
7. Покровская Е. Н., Портнов Ф. А., Кобелев А. А., Корольченко Д. А. Дымообразующая способность и токсичность продуктов сгорания древесных материалов при поверхностном модифицировании элементоорганическими соединениями // Пожаровзрывобезопасность. - 2013. - Т. 22, № 10.- С. 40-46.
8. Корольченко Д. А., Лукьянов А. М., Агапов А. Г. О пожароопасности древесины при возведении мостов // Мир транспорта. - 2012. - Т. 42, № 4. - С. 158.
9. Агапов А. Г., Корольченко Д. А. Промышленная безопасность при реконструкции и строительстве новых мостов // Вестник МГСУ. - 2011. - № 1-1. - C. 434-439.
10. Sharovarnikov A. F., Korolchenko D. A. Fighting fires of carbon dioxide in the closed buildings // Applied Mechanics and Materials.-2013.-Vol. 475-476.- P. 1344-1350. doi: 10.4028/www.scien-tific.net/amm.475-476.1344.
11. Gorshkov V.I., Korolchenko D. A., Shebeko Yu. N., Navtsenya V.Yu., Kostyukhin A. K. The peculiarities of application of gas-aerosol fire extinguishing tools in various rooms // Proceedings of Second International Seminar on Fire-and-Explosion Hazard of Substances and Venting of Deflagrations. - Moscow : All-Russian Research Institute for Fire Protection Publ., 1997. - P. 800-808.
12. Покровская Е. Н., Кобелев А. А., Нагановский Ю. К. Механизм и эффективность огнезащиты фосфоркремний органических систем для древесины // Пожаровзрывобезопасность. - 2009. - Т. 18, №3. -С. 44-48.
13. Кобелев А. А. Разработка комплексного огнебиовлагозащитного состава на основе соединений, обеспечивающих поверхностную модификацию древесины : дис.. канд. техн. наук. - М.: Академия ГПС МЧС России, 2012. - 128 с.
14. Покровская Е. Н., Кобелев А. А. Огнезащита древесины на современном этапе // Вестник Академии Государственной противопожарной службы. - 2007. - № 7. - С. 76 85.
15. ГОСТ 12.1.044-89*. ССБТ. Пожаровзрывоопасность веществ и материалов. Номенклатура показателей и методы их определения. - Введ. 01.01.91 г. - М. : Изд-во стандартов, 1989; ИПК "Изд-во стандартов", 1996; 2001.
16. Ролдугин В. И. Физикохимия поверхности : учебник-монография. -Долгопрудный : Изд. дом "Интеллект", 2011. - 568 с.
17. Кельцев Н. В. Основы адсорбционной техники : монография. -2-е изд., перераб. и доп. -М. : Химия, 1984. - 592 с.
18. Наканиси К. Инфракрасные спектры и строение органических веществ. - М.: Мир, 1965. - 219c.
19. Bikales N. M., Segal L. (eds.). Cellulose and cellulose derivatives. -New York : Wiley-Interscience, 1971. - 127 p.
20. Технический регламент о требованиях пожарной безопасности : Федер. закон от 22.08.2008 № 123-ФЗ (в ред. от 10.07.2012 № 117-ФЗ, 02.07.2013 № 185-ФЗ) // Собр. законодательства РФ. - 2008. - № 30 (ч. I), ст. 3579.
Review
For citations:
Pokrovskaya E.N., Portnov F.A., Kobelev A.A., Beltsova T.G. INFLUENCE OF SURFACE LAYER STRUCTURE FORMED DURING THERMAL DEGRADATION OF WOOD ON SMOKE GENERATION PROPERTY. Pozharovzryvobezopasnost/Fire and Explosion Safety. 2015;24(6):16-22. (In Russ.)
Views:
359
Email this article 