FEATURES THE TESTING OF AVIATION MATERIALS ON FIRE SAFETY. Part 1. Test on flammability - influence of sample thickness on registered characteristics

According to requirements of aviation norms, tests for definition characteristics of flammability under the influence of open flame samples of materials for all used thickness are subject. For the purpose of tests volume reduction, foreign researchers have makes the decision that "Data from testing a thinner construction substantiates a thicker construction made ofthe same materials". Researches on influence of sample thickness of polymeric composite materials and core panels on their basis on flammability characteristics (burn-out length, duration of residual independent burning) according to requirements of aviation norms are conducted. In this article the characteristics of flammability for different types polymeric materials of aviation assignment (glass-, organ- and carbon reinforced plastics, core panels) were analyzed. The obtained experimental data show that the accepted assumption is carried out for burn-out length, but not always operates for the characteristic of duration of residual burning. It is offered at performance of qualification tests on flammability to use the standard number of thickness similar to applied at definition the smoke and heat release characteristics.

горючесть, остаточное горение, длина прогорания, полимерный композиционный материал, сотовая панель, толщина образца, flammability, residual burning, burn-out length, polymeric composite material, core panel, sample thickness

1. Sarkos G. Evolution of FAA Fire Safety R&D Over the Years // The Fifth Triennial Fire & Cabin Safety Research Conference, 29 October -1 November 2007, Atlantic City, NJ. URL: http://www.fire.tc.faa.gov/ 2007Conference/files/General_Fire/TueAM/SarkosFAAFire/SarkosFAAFirePres.pdf (дата обращения: 30.09.2014 г.).

2. Нормы летной годности гражданских самолетов СССР. - 2-е изд. - М. :ЦАГИ, 1974. - 344 с.

3. Aircraft Materials Fire Test Handbook // DOT/FAA/AR-00/12. - 235 p.

4. Барботько С. Л. Пожаробезопасность авиационных материалов // Авиационные материалы и технологии. - 2012.-№S. - C 431-439.

5. Барботько С. Л., Кириллов В. Н., Шуркова Е. Н. Оценка пожарной безопасности полимерных композиционных материалов авиационного назначения // Авиационная промышленность. - 2013.-№2. - С. 55-58.

6. Авиационные правила. Часть 25. Нормы летной годности самолетов транспортной категории / МАК. - М. : ОАО "Авиаиздат", 2009. - 267 с.

7. Marker T. Update Handbook Chapters // International Aircraft Materials Fire Test Working Group, 23 June 2010, Cologne, Germany. - 15 p. URL : https://www.fire.tc.faa.gov/pdf/materials/ June10Meeting/marker-0610-Part25Update.pdf (дата обращения: 30.09.2014 г.).

8. Campbell S., Jensen M. Flammability standardization task group // The Sixth Triennial International Fire & Cabin Safety Research Conference, 25-28 October 2010, Atlantic City, NJ. - 28 p. URL : https://www.fire.tc.faa.gov/2010Conference/files/Materials_Safety_Development_II/Campbell-Standardization/CampbellStandardizationPres.pdf (дата обращения: 30.09.2014 г.).

9. Gardlin J. A threat-based approach to part 25 flammability regulations // The Sixth Triennial International Fire & Cabin Safety Research Conference, 25-28 October 2010, Atlantic City, NJ. - 22 p. URL: http://www.fire.tc.faa.gov/2010Conference/files/Aircraft_Fire_Safety/GardlinPart25/GardlinPart25-Pres.pdf (дата обращения: 30.09.2014 г.).

10. QuintiereJ. G., Downey B. P., Lyon R. E. An investigation of the vertical Bunsen burner test for flammability of plastics // FAA Report DOT/FAA/AR-TN11/19. - 2012. - 20 p.

11. Cambell S., Jensen M., Sattayatam P. Flammability standardization task group - Final reports: Federal Aviation Administration Draft Policy Memo, AMN-115-09-XXX, 20 August 2009 // FAA Report DOT/FAA/TC-12/10. - 2012. - 881 p.

12. Барботько С. Л., Швец Н. И., Застрогина О. Б., Изотова Т. Ф. Исследование влияния толщины стеклопластиков на характеристики тепловыделения при горении // Пожаровзрывобезопасность. - 2013. - Т. 22, №№ 7. - С. 30-36.

13. Барботько С. Л., Воробьёв В. Н. Пожаробезопасность авиационных материалов и элементов конструкций : справочник. - М. : ВИАМ. 2007. - 543 с.

14. Каблов Е. Н. Стратегические направления развития материалов и технологий их переработки на период до 2030 года // Авиационные материалы и технологии. - 2012. - № S. - С. 7-17.

15. Каблов Е. Н. Материалы и химические технологии для авиационной техники //ВестникРоссий-ской академии наук. - 2012. - Т. 82, № 6. - С. 520-530.

16. Дементъева Л. А., Сереженков А. А., Лукина Н. Ф., Куцевич К. Е. Клеевые препреги и слоистые материалы на их основе // Авиационные материалы и технологии. - 2013. - №2. - С. 19-21.

17. Застрогина О. Б., Швец Н. И., Постнов В. И., СерковаЕ. А. Фенолформальдегидные связующие нового поколения для материалов интерьера // Авиационные материалы и технологии. - 2012. - № S. - С. 265-272.

18. Давыдова И. Ф., Кавун Н. С. Стеклопластики - многофункциональные композиционные материалы // Авиационные материалы и технологии. - 2012. - № S. - С. 253-260.

19. Кондратов Э. К., Постнов В. И., Петухов В. И., Кавун Н. С., Абрамов П. А., Юдин А. А., Барботь-ко С. Л. Исследование свойств трехслойных панелей на модифицированном связующем ФПР-520Г // Авиационные материалы и технологии. - 2009.-№3.-С.19-23.

20. БорщевА. В., Хрульков А. В., Халтурина Д. С. Изготовление низкопористого полимерного композиционного материала для применения в слабо- и средненагруженных конструкциях // Труды ВИАМ. - 2014. -№ 7, ст. 03. URL : http://www.viam-works.ru/plugins/content/journal/uploads/ articles/pdf/682.pdf (дата обращения: 30.09.2014 г.).

21. Гуляев И. Н., Власенко Ф. С., Зеленина И. В.,РаскутинА. Е. Направления развития термостойких углепластиков на основе полиимидных и гетероциклических полимеров // Труды ВИАМ. - 2014. -№ 1, ст. 04. URL: http://www.viam-works.ru/plugins/content/journal/uploads/articles/pdf/ 636.pdf (дата обращения: 30.09.2014 г.).

22. Бейдер Э. Я., Петрова Г. Н., Изотова Т. Ф., Барботько С. Л. Стеклопластики на термопластичной матрице // Труды ВИАМ. - 2013. -№7, ст. 03. URL : http://www.viam-works.ru/plugins/ content/journal/uploads/articles/pdf/116.pdf (дата обращения: 30.09.2014 г.).

23. Пат. 2447104 Российская Федерация. МПК C08L 63/00, C08K 5/103, B29 B15/10. Эпоксидная композиция / Мухаметов Р. Р., АхмадиеваК. Р.,Чурсова Л. В., КабловЕ. Н., Хрульков А. В., Ду-шин М. И. - № 2010140692/05; заявл. 05.10.2010 г.; опубл. 10.04.2012 г., Бюл. № 10.